Provil® Novo putty und putty soft

The Kneadable
The addition- crosslinking silicones consist of a base and a catalytic component and can be kneaded by hand at a mixing ratio of 1:1. To produce an impression, simply apply the compound by hand on the surface to be examined. After about 4.5 to 5 minutes, the silicone is sufficiently cured to be removed. The main difference between the two products is the final hardness.(see technical data). A typical application is the impression taking for measuring in the mould and toolmaking industry. There is no need for special prior knowlegde for the application.

PROVIL NOVO PUTTY AND PROVIL NOVO PUTTY SOFT ARE USED FOR IMPRESSIONS

Where large surfaces must be casted
At hard to acccess places or when working overhead
To stabilize making impressions with the flexible Provil novo Light ( double impression technique)

ORDER INFORMATION PROVIL NOVO PUTTY REGULAR & PUTTY SOFT

66003628 PROVIL® NOVO
450 ml base,450 ml cat.

66004372 PROVIL® novo putty soft
450 ml base, 450 ml cat.

PROPERTIES AND APPLICATION

Easy application procedures preventing errors
Colour-coded puttiies and scoops eliminate mixing errors
Ready in seconds after mixing
Impressions can be evaluated with measuring probes or non- contact measuring methods
Provil novo can be removed without leaving any residue on the specimen

DID YOU KNOW…
that perfect results can be achieved using a combination of Provil novo light and putty. Minimum shrinkage , great accuracy to detail.

Technical Data Silicone Impression Materials

Product	Provil novo putty	Provil novo putty soft	Provil novo l ight
Mixing time	45 sec.	45 sec.	—-
Total processing measured from start of mixing	2 min.	2 min.	2 min.
Setting time measured from start of mixing	4:45 min.	4:45 min.	4:30 min.
Deformation under pressure	0.8 – 5.0%	0.8 – 5.0 %	2.0-5.0 %
Recovery from deformation	99.70 %	99.70 %	99.80 %
Hardness test Shore-A (measured from start of mixing)	After 10 min. : 70 1hour: 71 24 hour: 71	After 10 min. : 57 1hour:57 24 hour: 60	After 10 min. : 52 1 min. : 52 24 min: 52

Technical data light curing impression materials

Product	Technovit 2200	Technovit 2210	Technovit 2220
Colour	Opaque-transparent	Cream- coloured	Blue or transparent
Container	Glass bottle	Syringe	Jar
Viscosity	Low	Medium	Medium
Polymeration type	Light curing (blue light)	Light curing (blue light)	Light curing (blue light)
Bending strength	90-100 N/mm²	>100 N/mm²	104.00 Mpa
Bending module hardness Hz	3.500- 4.500 N/mm² 180 – 200 N/mm²	5.000 -6.000 N/mm² 180-200 N/mm²	2.321 Mpa 120-150 N/mm²
Curing depth	4mm (Pekalux POWER LED. 20 sec.) 7 mm (Technovit Blue LED.40 sec.)	4 mm (Pekalux POWER LED. 20 sec.) 5 mm (Technovit Blue LED.40 sec.)	7 mm (Pekalux POWER LED. 40 sec.) 7 mm (Technovit Blue LED.60 sec.)